| 书目名称 | Damage and Fracture of Ceramic-Matrix Composites Under Stochastic Loading |
| 编辑 | Longbiao Li |
| 视频video | |
| 概述 | Provides micromechanical models for tensile, fatigue, and stress-rupture behavior of fiber-reinforced ceramic-matrix composites (CMCs) subjected to stochastic loading.Predicts experimental results of |
| 丛书名称 | Advanced Ceramics and Composites |
| 图书封面 |  |
| 描述 | .This book presents the relationships between tensile damage and fracture, fatigue hysteresis loops, stress-rupture, fatigue life and fatigue limit stress, and stochastic loading stress. Ceramic-matrix composites (CMCs) possess low material density (i.e., only 1/4 - 1/3 of high-temperature alloy) and high-temperature resistance, which can reduce cooling air and improve structure efficiency. Understanding the failure mechanisms and internal damage evolution represents an important step to ensure reliability and safety of CMCs. This book investigates damage and fracture of fiber-reinforced ceramic-matrix composites (CMCs) subjected to stochastic loading, including: (1) tensile damage and fracture of fiber-reinforced CMCs subjected to stochastic loading; (2) fatigue hysteresis loops of fiber-reinforced CMCs subjected to stochastic loading; (3) stress rupture of fiber-reinforced CMCs with stochastic loading at intermediate temperature; (4) fatigue life prediction of fiber-reinforced CMCssubjected to stochastic overloading stress at elevated temperature; and (5) fatigue limit stress prediction of fiber-reinforced CMCs with stochastic loading. This book helps the material scientists and |
| 出版日期 | Book 2021 |
| 关键词 | Ceramic-matrix composites (CMCs); Hysteresis loops; Stress-rupture; Fatigue life; Fatigue limit stress; S |
| 版次 | 1 |
| doi | https://doi.org/10.1007/978-981-16-2141-3 |
| isbn_softcover | 978-981-16-2143-7 |
| isbn_ebook | 978-981-16-2141-3Series ISSN 2662-9305 Series E-ISSN 2662-9313 |
| issn_series | 2662-9305 |
| copyright | The Editor(s) (if applicable) and The Author(s), under exclusive license to Springer Nature Singapor |
发表于 2025-3-21 16:31:02