书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength影响因子(影响力)<br> http://figure.impactfactor.cn/if/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength影响因子(影响力)学科排名<br> http://figure.impactfactor.cn/ifr/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength网络公开度<br> http://figure.impactfactor.cn/at/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength网络公开度学科排名<br> http://figure.impactfactor.cn/atr/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength被引频次<br> http://figure.impactfactor.cn/tc/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength被引频次学科排名<br> http://figure.impactfactor.cn/tcr/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength年度引用<br> http://figure.impactfactor.cn/ii/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength年度引用学科排名<br> http://figure.impactfactor.cn/iir/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength读者反馈<br> http://figure.impactfactor.cn/5y/?ISSN=BK0460290<br><br> <br><br>书目名称IIW Guidelines on Weld Quality in Relationship to Fatigue Strength读者反馈学科排名<br> http://figure.impactfactor.cn/5yr/?ISSN=BK0460290<br><br> <br><br>
把手
发表于 2025-3-21 23:40:33
IIW Guidelines on Weld Quality in Relationship to Fatigue Strength978-3-319-19198-0Series ISSN 2365-435X Series E-ISSN 2365-4368
finite
发表于 2025-3-22 00:32:24
http://reply.papertrans.cn/47/4603/460290/460290_3.png
lethal
发表于 2025-3-22 06:57:24
Introduction,Complex welded structures are frequently exposed to demanding fatigue loading during service. In recent years, the Commission XIII of the International Institute of Welding (IIW) has developed several documents related to the analysis and design of welded structures to resist fatigue failure.
走路左晃右晃
发表于 2025-3-22 09:25:53
Design for Purpose,Typical fabricated structures may have hundreds or even thousands of meters of weld. Thus, many potential fatigue cracking locations are present that must be considered during design development and production.
anniversary
发表于 2025-3-22 14:27:20
http://reply.papertrans.cn/47/4603/460290/460290_6.png
macrophage
发表于 2025-3-22 17:38:35
Root Side Requirements,When designing a weld, it is often desirable that the root side has a greater or at least the same fatigue life as the toe side.
Concerto
发表于 2025-3-22 22:14:01
Inspection, Quality Control, and Documentation,Fatigue in welds is to a great extent governed by geometric issues. This includes not only the local size of things in the weld but also all kinds of irregularities and imperfections that can be found and which are named in the language of the workshop as defects.
CURB
发表于 2025-3-23 01:25:40
http://reply.papertrans.cn/47/4603/460290/460290_9.png
lipoatrophy
发表于 2025-3-23 07:52:07
Bertil Jonsson,G. Dobmann,G. MarquisProvides quantitative and qualitative measures of the geometric features and imperfections of welds.Defines more restrictive acceptance criteria based on weld geometry features and imperfections with