Application of Thermodynamic and Kinetic Parameters of the V-O-Na System to the Sodium Corrosion of breeder reactor. While there is considerable disagreement in the reported corrosion behavior of candidate alloys,. the importance of nonmetallic impurities (O, N, H, and C) in sodium on the predominant corrosion processes is generally recognized. Much of the disagreement can be attributed to the ina
慷慨不好
发表于 2025-3-30 12:58:15
Corrosion of Oxygen Contaminated Tantalum in NaKted by small amounts of oxygen..SNAP-8 boilers under evaluation employ NaK in a thermal bond annulus. This NaK contacts both tantalum tubing and weldments and it is therefore important to determine the effect of the oxygen concentration of tantalum on its corrosion resistance to NaK..Tantalum specim
CRACK
发表于 2025-3-30 16:59:40
Penetration of Refractory Metals by Alkali Metalsanes. Penetration is observed only when oxygen dissolved in the refractory metal exceeds some threshold concentration. This concentration depends upon the refractory metal, the alkali metal, and the temperature. Penetration was first encountered in niobium and tantalum exposed to lithium, but has no
不自然
发表于 2025-3-30 21:29:53
http://reply.papertrans.cn/24/2388/238799/238799_54.png
PAGAN
发表于 2025-3-31 01:08:12
http://reply.papertrans.cn/24/2388/238799/238799_55.png
prostate-gland
发表于 2025-3-31 07:44:45
The Corrosion of Metals by Molten Lithiumhium on microstructure, tensile strength, and stress corrosion was found. The austenitic stainless steels, types 302, 303, 304, 316, 347 and the ferritic stainless steels, types 446, 430, 405 apparently were not impaired. Hardenable stainless steels were corroded when hardened but not when annealed.
营养
发表于 2025-3-31 11:52:30
http://reply.papertrans.cn/24/2388/238799/238799_57.png
Estimable
发表于 2025-3-31 15:44:52
http://reply.papertrans.cn/24/2388/238799/238799_58.png
小母马
发表于 2025-3-31 18:49:24
http://reply.papertrans.cn/24/2388/238799/238799_59.png
僵硬
发表于 2025-3-31 22:52:14
Corrosion Studies of Liquid Metal Heat Pipe Systems at 1000° to 1800°Crefractory metal seamless tubing have been conducted in vacuum at temperatures of 1000° to 1800°C and at times to 1000 hours. Systems evaluated to date are: TZM with indium; Cb-1Zr with lead, calcium, and barium; and Ta-10W with indium, calcium, lead, thallium, and barium. The observed corrosion beh